Standard of Aluminum Alloy Architectural Profile

- Dec 18, 2017 -

Strictly control the quality according to national standard GB5237-2008 of Aluminum Alloy Architectural Profile.



Raw material national standard

Trade Mark and 

State

6063 T5
Standard No.GB5237.1-2008

Appearance 

Quality

1.The surface of the sectional material should be neat, and no presence of such defects of crackles

peeling, corrosion, bubbles, etc..

2.It is allowed to have slight pressed dents, bumps and abrasion on the surface of the sectional 

material. Their allowable depth is not greater than 0.07mm for a decorative surface, and is not 

greater than 0.10mm for a non-decorative surface, and the depth of an extruded mark of a 

mould is not greater than 0.03mm.

3.An end of the sectional material is allowed to have local deformation due to being sawed, 

and its vertical length should not exceed 10mm.

Allowable 

Deviation

and High Accuracy 

of Dimensions

Level clearance

Degree 

of curvature

TorsionAngleLength

On a random 

25m width≤

0.15mm

On a random

 300m length≤0.3mm

On the 

length of 

each meter≤1.2mm

±1°Nominal length≤6m±15mm

Mechanical 

Properties

Webster

 hardness(HW)

Tensile strengthYield strength

Elongation

 percentage


≥8≥160N/mm2≥110N/mm20.08

Chemical 

Compositions

SiFeCuMnMgZnImpurity
SingleTotal
0.2-0.6≤0.35≤0.20≤0.050.45-0.90≤0.05≤0.05≤0.15


Anodizing national standard

Trade Mark and 

State

6063 T5
Standard No.GB5237.2-2008

The quality of 

the base material

Should accord with the GB5237.1-2008 regulations

The allowable 

deviation of the 

dimensionss

Should accord with the GB5237.1-2008 regulation

The mechanical 

properties

Should accord with the GB5237.1-2008 regulations

The chemical 

compositions

Should accord with the GB5237.1-2008 regulations

Oxide Film 

Quality


Average film 

thickness

Minimum 

local

 film thickness

CASS test

Alkaline 

dropping

 corrosion 

resistance test

Abrasion 

coefficient

 of 

sand 

trial

Sealed hole
AA10 grade≥10μm≥8μm≥9grade≥50S≥300g/μm≤30mg/dm2
AA15 grade≥15μm≥12μm≥9grade≥75S≥300g/μm
Appearance quality

A surface is not allowed to have such defects as slight burns, coming off of oxide film, etc.,

which influence the use.Within 8 m from an end of the sectional material, it is allowed to 

have no film locally and electric burns


Electrophoresis national standard

Trade Mark and 

State

6063 T5
Standard No.GB5237.3-2008

The quality of the 

base material

Should accord with the GB5237.1-2008 regulations

The allowable deviation

of the dimensionss

Should accord with the GB5237.1-2008 regulation

The mechanical 

properties

Should accord with the GB5237.1-2008 regulations

The chemical 

compositions

Should accord with the GB5237.1-2008 regulations

Quality of 

Complex Film


Anode oxide

 film

Paint filmComplex film

Paint the membrane


Local film

 thickness

Local film

 thickness

Local 

film thickness

Adhesive forceHardness
A≥9μm≥12μm≥21μm0grade≥3H
B≥9μm≥7μm≥16μm0grade≥3H

Appearance 

quality

Before applying paint, the appearance quality of the sectional material should accord

with the relevant regulations of GB. The finished paint film should be even and neat, 

and it is not allowed to have such defects as wrinkle , crackles, bubbles, flowing marks, 

inclusions , sticking and coming off of paint film, etc, which influences the use, but in 

the 8m range of an end of the electrophoresis sectional material , it is allowed to have

no paint film locally.


Power coating national standard

Trade Mark and 

State

6063 T5
Standard No.GB5237.4-2008

The quality of the 

base material

Should accord with the GB5237.1-2008 regulations

The allowable 

deviation of the 

dimensionss

Should accord with the GBGB5237.1-2008 regulation

The mechanical 

properties

Should accord with the GB5237.1-2008 regulations

The chemical 

compositions

Should accord with the GB5237.1-2008 regulations

Coating 

Performance

1.Minimum local thickness
≥40μm
2.Color and color difference

The color of the coating should be the same as the standard color that the contract stipulates. 

aberration △Eab·≤1.5.

3.Indentation hardness (Print resistance)
≥80
4.Adhesive force
0grade
5.Impact resistance

The front of the coating, after an impact test, has no phenomenon of fracture and coming off,

but it is allowed to have small wrinkles in the perimeter of a concave surface.

6.Cup-drawing test 

After a cup-drawing test with of the indentation depth of 6mm, there should not be the 

phenomena of splitting and coming off on the coating.

7.Appearance quality

The coating of a decorative surface of the powder-sprayed sectional material should be 

smooth and even, and it is not allowed to have such defects as flowing marks, swelling

bubbles, crackles, sticking, etc, which influence the use.It is allowed to have a slight 

tangerine peel phenomenon, and the degree that is allowed should be indicated by a

guide sample of a material object which both the supplying and demanding sides 

have agreed on.